Kupanga na kugwiriskira ncito kwa kusintha kwa vitsulo vya manganese kwakusinthika - Kumanya

Kupanga kemiko na kugwiriskira ncito vitsulo vyakusinthika vya manganese .

limestone hammer crusher hammer head

mutundu wa munthu	grade ya chisulo		Chigaŵa cha mtundu wa mtundu wa mtundu wa mtundu wa pulogiramu %) .						wili kugwiriskira ncito .
mutundu wa munthu	grade ya chisulo		C	Si	Mn	Mo	cr	vinyakhe	wili kugwiriskira ncito .
China	Mn6Mo		1.2-1.4	0.4-0.7	5.5-7.0	0.8-1.2 1.5	(Chigaŵa chichoko) (chigaŵa chikuru)	-	Iwo ŵakunozga vipangizo vya makala vya makala na makina ghakuzenga .
America	Climax 6Mn-1o	kilasi A	1.05-1.35	0.40-0.70	5.75-6.75	0.90-1.20	vyakukhala	-
America	Climax 6Mn-1o	gore B	0.80-1.00	0.40-0.70	6.00-7.00	0.90-1.20	vyakukhala	-
China	5Cr5Mni		0.54	-	8.86	-	4.94	-	Kuponya matope na mtenje wakuphwanyika wa mano ghakuponyeka, mino gha shovel gha magesi
	60Cr5M1111 .		0.58	-	11.0	-	4.7	-
	Mnn9Cr)		-	-	-	-	-	-
	45Mn17A3		0.34-0.42	0.27-0.57	17.2-18.0	-	-	Al:2.77-3.20 Ti:0.078-0.098	Kugwira ntchito na nkhongono zakukhwaska chomene, nga ni nyundo ya dontho na base yake .
	7M133		0.7-0.8	Kujumpha panji kulingana na 0.5 .	12.5-14.5	-	-	Ti: Kujumpha panji kufanana na 0.1.	Gwiliskirani nchito pasi pa mtundu wa cast. Baji yakufukura chomene, kapangilo kakusuzga ka bolodi la gridi, bolodi la lining, na vinyake

Manganese Steel (chisulo chikuru cha manganese)

Chitsulo cha alloy chili na manganese ghakujumpha 10%. Mu 1882, wakapokera chitsulo cha manganese chapachanya cha bungwe la austenitic, ndipo mu 1883, British Hadfield (RAHadfield) yikasanga patent ya chisulo cha manganese chapachanya. Pamwamba-} munganizoni kungagaŵika mu vigaŵa viŵiri mwakuyana na kugwiriskira ncito kwake kwakupambanapambana:

(1) Vwarani- zitsulo izo zikuleka kukhalirapo. Mtundu uwu wa zitsulo uli na 10% ~ 15% manganese, ndipo carbon iyo yili mu mtundu uwu njakukwana, chomenechomene 0.90% ~ 1.50%, vinandi vyake ni vyakujumpha 1.0%. Kupanga kwake kwa kemiko ni (%):

C0.-90-1. 50Mn10.0-15-0-15.

Si0.30 ~ 1.0 S 0.05 P 0.10 Mtundu uwu wa chisulo cha manganese chapachanya ndiwo ukugwiriskirika nchito chomene, uwo ukugwiriskirika nchito chomene pakupanga mino ghakufukura, khoma lakugubuduka na khoma lakuphwanyika la cone crusher, m'kamwa pa bolodi la m'kamwa, bolodi la mphero ya ball, switch ya ball, nyundo ya mbale, nyundo, mutu wa nyundo, na vinyake.

Viŵaro vya cast vya vitsulo vya mangangasese kanandi vikupangika na austenite, carbide na ngale, ndipo nyengo zinyake vikuŵa na phosphorus co- crystals. Chiŵelengero cha carbide chili chikuru, kanandi chikuwoneka mu netiweki pa mphaka ya tirigu. Ntheura, chisulo cha mangangas mu viwaro vyakuponyeka ni chakuphwanyika ndipo chingagwiliskirika ntchito yayi ndipo chikukhumbikwira wovwiri wakukhora. Nthowa iyo yikugwiriskirika nchito comene pa nyengo yakutenthemeska ya mtundu wa mtundu, apo cisulo cikutenthemeska kufika pa 1050 ~ 1100℃, kutetezga kuti vifumiske viŵaro vya cast, sangani viwaro vya austenitic, ndipo viwaro, ndipo viwaro vikuzimika, mwakuti viŵaro visungike ku kutentha kwa chipinda. Pamanyuma pa kutenthemeska, nkhongono, pulasitiki na kukhora kwa visulo vikusintha chomene, ntheura nthowa iyi yakuchizgira kutentha kanandi yikuchemekaso kuti kuchizga kwa maji ghakukhora. Pamanyuma pa kutenthemeska kwa kutentha, katundu wa makina: σ b615 ~ 1275MPa σ 0.2340 ~ 470MPa ζ15% ~ 85% ψ 15% ~ 45% a Kl 96 ~ 294 J / cm2 HBl80 ~ 225

Pamanyuma pa wovwiri wakukhora, pazamuŵa carbide yichoko waka iyo yikusungunuka yayi, iyo yingagwiliskirika nchito para ndalama izo zilipo ni zicoko ndipo zikukwaniska vigaŵa vya mayeso.