Kutentha {{0} Kupona kwa Ndege za Injini za Aeronautical
1. GH2132 (Iconnel 718)
Kapangidwe ka vinthu: Ni 55-58%, Cr 17-21%, Mo 2.8-3.3%, Nb 4.75-5.5%, Ti 0.65-1.15%, Al 0.2-0.8%
Nkhongono: HRC 30-45
Kutentha-resistant kutentha kwa msinkhu wa kutentha: -253 digiri kufika pa 700 degree
2. GH4169 (Iconel 625)
Vinthu vyakupangika: Ni 58%, Cr 20%, Mo 8%, Ti 3.8%, Al 1.9%
Nkhongono: HRC 34-40
Kutentha-resistant kutentha kwa msinkhu: -253℃kufika pa 1000 degree
1. Kutentha- chisulo chakupangika na mafakitale gha mafuta
1.1C55Mo (P5) Vinthu vyakupangika: C 0.15%, Si Kukhala Kuchoko panji kufanana na 0.50%, Mn0.30 - 0.60%, Cr4.00 - 6.00%, Mo 0.45 - 0.65% Nkhongono: HB Less kuluska panji yakuyana waka na 187 Heat- kutentha kwakutentha: -29 digiri kufika pa 550 degrees kufika pa 550℃ku 550℃1.
2. 15CrMo (P11) Vinthu vyakupangika: C 0.12-0.18%, Si 0.17-0.37%, Mn 0.40-0.70%, Cr 0.80-1.10%, Mo 0.40-0.55%. Nkhongono: HB Kuchepa panji kufanana na 217. Kutentha kwa kutentha kwa kutentha: -29℃kufika pa 550℃.
Heat{{0} }erismont zitsulo kwa maboyilo na viŵiya vyakupanikizgika .
1.15CHENJEZGANI Vinthu vyakupangika: C 0.12-0.18%, Si 0.17-0.37%, Mn 0.40-0.70%, Cr 0.80-1.10%, Mo 0.40-0.55%. Nkhongono: HB Kuchepa panji kufanana na 217. Kutentha kwa kutentha kwa kutentha: -29℃kufika pa 550℃.
2. 13CrMo44 Kupangika kwa vinthu: C 0.15-0.18%, Si Kukhalaso panji kufanana na 0.50%, Mn 0.40-0.70%, Cr 0.70-1.10%, Mo 0.40-0.60%. Nkhongono: HB Kuchepa panji kufanana na 229. Kutentha kwa kutentha kwa kutentha: -29℃kufika pa 550℃. Ivyo vyayowoyeka pacanya apa ni vigaŵa vinyake vya visulo ivyo vikuzizipizga kutentha na vigaŵa vyawo vya kutentha. Ma grade agha ghose ghali na katundu munyake wakulimbana nayo, kweni kusankha kwapadera kukukhumbikwira kughanaghanirika mwakukwana mwakuyana na malo ghakugwilira ntchito na ivyo vikukhumbikwa.